zhpsЖурнал прикладной спектроскопииZhurnal Prikladnoii Spektroskopii0514-7506B. I. Stepanov Institute of Physics of the National Academy of Scienceszhps-881Research ArticleАННОТАЦИИ АНГЛОЯЗЫЧНЫХ СТАТЕЙABSTRACTS ENGLISH-LANGUAGE ARTICLESМикроструктура и красная люминесценция наночастиц/нановолокон ZnO, синтезированных методом электровытягивания с последующим термическим отжигомMicrostructure and red luminescence of ZnO nanoparticles/nanofibers synthesized by electrospinning followed by thermal annealingHuanP. V.HuanP. V.

Ханой

Hanoi

ThongN. D.ThongN. D.

Ханой

Hanoi

ThuyV. T. P.ThuyV. T. P.

Ханой

Hanoi

ToanL. V.ToanL. V.

Ханой

Hanoi

KienN. D. T.KienN. D. T.

Ханой

Hanoi

TuanT. Q.TuanT. Q.

Ханой

Hanoi

tuan.taquoc@hust.edu.vnPhamV.-H.PhamV.-H.

Ханой

Hanoi

vuong.phamhung@hust.edu.vnПередовой институт науки и техники (AIST) при Ханойском университете науки и техники (HUST)Advanced Institute for Science and Technology (AIST) at Hanoi University of Science and Technology (HUST)Передовой институт науки и техники (AIST) при Ханойском университете науки и техники (HUST); Школа инженерной физики Ханойского университета науки и техники (HUST),Advanced Institute for Science and Technology (AIST) at Hanoi University of Science and Technology (HUST); School of Engineering Physics at Hanoi University of Science and Technology (HUST)Передовой институт науки и техники (AIST) при Ханойском университете науки и техники (HUST); Университет профсоюзовAdvanced Institute for Science and Technology (AIST) at Hanoi University of Science and Technology (HUST); Trade Union UniversityПередовой институт науки и техники (AIST) при Ханойском университете науки и техники (HUST); Технический университет Ле Куй ДонаAdvanced Institute for Science and Technology (AIST) at Hanoi University of Science and Technology (HUST); Le Quy Don Technical University202126072021884665670Copyright © Huan P.V., Thong N.D., Thuy V.T., Toan L.V., Kien N.D., Tuan T.Q., Pham V., 20212021Huan P.V., Thong N.D., Thuy V.T., Toan L.V., Kien N.D., Tuan T.Q., Pham V.Huan P.V., Thong N.D., Thuy V.T., Toan L.V., Kien N.D., Tuan T.Q., Pham V.Данная работа распространяется под лицензией Creative Commons Attribution 4.0.This work is licensed under a Creative Commons Attribution 4.0 License.https://zhps.ejournal.by/jour/article/view/881

Изучена красная видимая люминесценция нановолокон ZnO, синтезированных методом электровытягивания с последующим термическим отжигом при температуре 600 °C. Нановолокна ZnO получены путем электровытягивания смеси предшественника ацетата цинка — поливинилпирролидона (ПВП), с использованием различных концентраций ПВП. Диаметр нановолокна ZnO зависит от концентрации ПВП и увеличивается по мере роста концентрации ПВП. Термический отжиг вызывает значительные изменения в нановолокнах ZnO, которые формируют структуры наночастиц/нановолокон ZnO в зависимости от концентрации ПВП. Нановолокна ZnO, синтезированные с концентрацией ПВП 20 %, индуцируют однородное распределение наночастиц ZnO с высокой ин- тенсивностью видимой люминесценции вблизи ~650 нм. Показано, что электровытягивание с последующим термическим отжигом может быть важным методом синтеза наночастиц ZnO/нановолоконных структур, которые могут применяться в передовой технике — оптоэлектронике и зондировании. 

This paper reports the red visible luminescence of ZnO nanofibers synthesized by electrospinning followed by thermal annealing. The ZnO nanofibers were prepared by electrospinning of the precursor mixture of zinc acetate/polyvinylpyrrolidone (PVP) by using different PVP concentrations, while thermal annealing was kept at 600°C. The ZnO nanofiber diameter was dependent on the PVP concentrations, which increased as PVP concentrations increased. Thermal annealing induced significant changes in ZnO nanofibers, which formed ZnO nanoparticle/nanofiber structures as a function of PVP concentrations. The ZnO nanofibers synthesized with PVP concentration of 20% induced homogeneous distribution of ZnO nanoparticles with highly visible luminescence intensities centering at ~650 nm. Results indicated that the use of electrospinning followed by thermal annealing could be an important method for the synthesis of ZnO nanoparticle/nanofiber structures, which could be used in advanced engineering such as optoelectronics and sensing. 

нановолокнолюминесценцияZnOвидимый светнаночастицаnanofiberluminescenceZnOvisible-lightnanoparticlesThis research is funded by Hanoi University of Science and Technology (HUST) under grant number T2018-PC-201.ReferencesZ. R. Dai, Z. W. Pan, Z. L. Wang, Adv. Funct. Mater., 13, 9–24 (2013).Z. R. Dai, Z. W. Pan, Z. L. Wang, Adv. Funct. Mater., 13, 9–24 (2013).J. Lian, Z. Ding, F. L. Kwong, D. H. L. Ng, Cryst. Eng. Commun., 13, 4820–4822 (2011).J. Lian, Z. Ding, F. L. Kwong, D. H. L. Ng, Cryst. Eng. Commun., 13, 4820–4822 (2011).Q. Tang, W. Zhou, J. Shen, W. Zhang, L. Kong, Y. Qian, Chem. Commun., 10, 712–713 (2004).Q. Tang, W. Zhou, J. Shen, W. Zhang, L. Kong, Y. Qian, Chem. Commun., 10, 712–713 (2004).M. McCune, W. Zhang, Y. Deng, Nano Lett., 12, 3656–3662 (2012).M. McCune, W. Zhang, Y. Deng, Nano Lett., 12, 3656–3662 (2012).D. Yuvaraj, K. Narasimha Rao, K. Barai, Solid State Commun., 149, 349–351 (2009).D. Yuvaraj, K. Narasimha Rao, K. Barai, Solid State Commun., 149, 349–351 (2009).W. Wang, B. Zeng, J. Yang, B. Poudel, J. Huang, M. J. Naughton, Z. Ren, Adv. Mater., 18, 3275–3278 (2006).W. Wang, B. Zeng, J. Yang, B. Poudel, J. Huang, M. J. Naughton, Z. Ren, Adv. Mater., 18, 3275–3278 (2006).V. H. Pham, V. T. Kien, P. D. Tam, P. T. Huy, Mater. Sci. Eng: B, 209, 17–22 (2016).V. H. Pham, V. T. Kien, P. D. Tam, P. T. Huy, Mater. Sci. Eng: B, 209, 17–22 (2016).S. Cho, J. Ma, Y. Kim, Y. Sun, G. K. L. Wong, J. B. Ketterson, Appl. Phys. Lett., 75, 2761 (1999).S. Cho, J. Ma, Y. Kim, Y. Sun, G. K. L. Wong, J. B. Ketterson, Appl. Phys. Lett., 75, 2761 (1999).A. Umar, B. K. Kim, J. J. Kim, Y. B. Hahn, Nanotechnology, 18, 175606 (2007).A. Umar, B. K. Kim, J. J. Kim, Y. B. Hahn, Nanotechnology, 18, 175606 (2007).S. S. Warule, N. S. Chaudhari, B. B. Kale, M. A. More, Cryst. Eng. Comm., 11, 2776–2783 (2009).S. S. Warule, N. S. Chaudhari, B. B. Kale, M. A. More, Cryst. Eng. Comm., 11, 2776–2783 (2009).V. Kumar, V. Kumar, S. Som, A. Yousif, N. Singh, O. M. Ntwaeaborwa, A. Kapoor, H. C. Swart, J. Colloid Interf. Sci., 428, 8–15 (2014).V. Kumar, V. Kumar, S. Som, A. Yousif, N. Singh, O. M. Ntwaeaborwa, A. Kapoor, H. C. Swart, J. Colloid Interf. Sci., 428, 8–15 (2014).H. Q. Wang, G. Z. Wang, L. C. Jia, C. J. Tang, G. H. Li, J. Phys. D: Appl. Phys., 40, 6549–6553 (2007).H. Q. Wang, G. Z. Wang, L. C. Jia, C. J. Tang, G. H. Li, J. Phys. D: Appl. Phys., 40, 6549–6553 (2007).D. Y. Jiang, J. X. Zhao, M. Zhao, Q. C. Liang, S. Gao, J. M. Qin, Y. J. Zhao, A. Li, J. Alloys Compd., 532, 31–33 (2012).D. Y. Jiang, J. X. Zhao, M. Zhao, Q. C. Liang, S. Gao, J. M. Qin, Y. J. Zhao, A. Li, J. Alloys Compd., 532, 31–33 (2012).D. H. Fan, W. Z. Shen, M. J. Zheng, Y. F. Zhu, J. J. Lu, J. Phys. Chem. C, 111, 9116–9121 (2007).D. H. Fan, W. Z. Shen, M. J. Zheng, Y. F. Zhu, J. J. Lu, J. Phys. Chem. C, 111, 9116–9121 (2007).R. Raji, K.G. Gopchandran, J. Sci.: Adv. Mater. Devic., 2, 51–58 (2017).R. Raji, K.G. Gopchandran, J. Sci.: Adv. Mater. Devic., 2, 51–58 (2017).A. B. Djurišić, Y. H. Leung, K. H. Tam, L. Ding, W. K. Ge, H. Y. Chen, S. Gwo, Appl. Phys. Lett., 88, 103107 (2006).A. B. Djurišić, Y. H. Leung, K. H. Tam, L. Ding, W. K. Ge, H. Y. Chen, S. Gwo, Appl. Phys. Lett., 88, 103107 (2006).M. Kitsara, O. Agbulut, D. Kontziampasis, Y. Chen, P. Menasché, Acta Biomater., 48, 20–40 (2017).M. Kitsara, O. Agbulut, D. Kontziampasis, Y. Chen, P. Menasché, Acta Biomater., 48, 20–40 (2017).Travis J. Sill, Horst A. von Recum, Biomaterials, 29, 1989–2006 (2008).Travis J. Sill, Horst A. von Recum, Biomaterials, 29, 1989–2006 (2008).C. Lai, X. Wang, Y. Zhao, H. Fong, Z. Zhu, RSC Adv., 3, 6640–6645 (2013).C. Lai, X. Wang, Y. Zhao, H. Fong, Z. Zhu, RSC Adv., 3, 6640–6645 (2013).E. Ghafari, Y. Feng, Y. Liu, I. Ferguson, N. Lu, Composites Part B, 116, 40–45 (2017).E. Ghafari, Y. Feng, Y. Liu, I. Ferguson, N. Lu, Composites Part B, 116, 40–45 (2017).H. Wu, W. Pan, J. Am. Ceram. Soc., 89, 699–701 (2006).H. Wu, W. Pan, J. Am. Ceram. Soc., 89, 699–701 (2006).J. Y. Park, S. S. Kim, J. Am. Ceram. Soc., 92, 1691–1694 (2009).J. Y. Park, S. S. Kim, J. Am. Ceram. Soc., 92, 1691–1694 (2009).D. Y. Lj2008).D. Y. Lj2008).A. Baez-Rodríguez, L. Zamora-Peredo, M. G. Soriano-Rosales, J. Hernandez-Torres, L. GarcíaGonzález, R. M. Calderón-Olvera, M. García-Hipólito, J. Guzmán-Mendoza, C. Falcony, J. Lumin., 218, 116830 (2020).A. Baez-Rodríguez, L. Zamora-Peredo, M. G. Soriano-Rosales, J. Hernandez-Torres, L. GarcíaGonzález, R. M. Calderón-Olvera, M. García-Hipólito, J. Guzmán-Mendoza, C. Falcony, J. Lumin., 218, 116830 (2020).J. Zhou, K. Nomenyo, C. C. Cesar, A. Lusson, A. Schwartzberg, C. C. Yen, W. Y. Woon, G. Leronde, Sci. Rep., 10, 4237 (2020).J. Zhou, K. Nomenyo, C. C. Cesar, A. Lusson, A. Schwartzberg, C. C. Yen, W. Y. Woon, G. Leronde, Sci. Rep., 10, 4237 (2020).Y. Kumar, A. K. Rana, P. Bhojane, M.Pusty, V. Bagwe, S. Sen, P. M. Shirage, Mater. Res. Express, 2, 105017 (2015).Y. Kumar, A. K. Rana, P. Bhojane, M.Pusty, V. Bagwe, S. Sen, P. M. Shirage, Mater. Res. Express, 2, 105017 (2015).