GAMMA-IRRADIATION INFLUENCE ON OPTICAL PROPERTIES OF POLYIMIDE-YBA₂CU₃O_6,7 SYSTEM

Influence of g-irradiation on the optical properties of a polyimide film and its polymer compositions with fillers from a dispersed powder of a high-temperature superconductor ҮBa₂Cu₃O_6.7 (YBaCuO) with a concentration of 0.05, 0.10 and 0.50% by weight was studied. It was established that γ-irradiation with a dose up to 600 kGy does not affect the transparency of polyimide films in the visible region of the spectrum. However, at irradiation doses of 250 and 600 kGy, a weakly expressed fine structure appears in the spectra of polyimide films in the range 220-300 nm, due to the contribution of the resulting diene structures to the optical transmission and the increased content of oxygen atoms. The YBaCuO filler and γ-irradiation cause the polyimide transition from the amorphous state to the crystalline state, which is manifested in a sharp change in the spectrum in the range of ~2.3-3.9 eV. A significant increase in the extinction coefficient was found in the composite containing 0.50% by weight of the filler that is associated with an increase in the radius of action of structurally active fillers on the macromolecules of the matrix.

полиимид, композитный материал, наполнитель, высокотемпературный сверхпроводник, оптические свойства, гамма-облучение, доза, polyimide, composite material, filler, high-temperature superconductor, optical properties, gamma irradiation, dose

1. V. Kravtsova, M. Umerzakova, N. Korobova, S. Timoshenkov, A. Matnishan, T. Akhnazaryan, R. Iskakov. 15th Int. Conf. Nanotechnol., 20 January 2016, Rome, IEEE (2016) 262-265

2. Е. П. Шешин, Л. В. Денисова. Вестн. Белгород. гос. технолог. ун-та им. В. Г. Шухова, № 12 (2016) 170-173

3. В. М. Станкевич, Ю. М. Плескачевский, В. В. Смирнов. Материалы 4-й междунар. конф. “Взаимодействие излучений с твердым телом”, 3-5 октября 2001 г., Минск, БГУ (2001) 297-299

4. С. Полесский, В. Жаднов, М. Артюхова, В. Прохоров. Компоненты и технологии, № 9 (2010) 93-98

5. М. Штейнберг, Е. А. Зенитова. Вестн. Казан. технолог. ун-та, № 8 (2012) 67-71

6. И. Н. Штефан, В. А. Лесничная, С. Р. Алляров, Ю. Н. Смирнов. Пласт. массы, № 12 (2012) 12-15

7. Ю. А. Михайлин. Термоустойчивые полимеры и полимерные материалы, С.-Петербург, Профессия (2006)

8. В. К. Крыжановский, В. В. Бурлов, А. Д. Паниматченко, Ю. В. Крыжановская. Технические свойства полимерных материалов, С.-Петербург, Профессия (2005)

9. S. Tomczak, D. Marchant, S. Svejda, T. Minton, K. Timothy, A. Brunsvold, E. Grossman, G. Schatz, D. Troya, L.-P. Sun, Li Peng, I. Gouzman. Properties and Improved Space Survivability of POSS (polyhedral oligomeric silsesquioxane) Polyimides, Technical Paper DARP A443 (2004) 12

10. A. C. Ferrari, B. Kleinsorge, G. Adamopoulos, J. Robertson, W. I. Milne, V. Stolojan, L. M. Brown, A. Libassi, B. K. Tanner. J. Non-Crystal. Solids, 266-269 (2000) 765-768

11. А. И. Купчишин, А. Д. Мурадов, Б. Г. Таипова, Р. М. Искаков, М. Абилова. Тр. 5-й междунар. науч. конф. “Радиационно-термические эффекты и процессы в неорганических материалах”, Томск, изд-во ТПУ (2006) 342-346

12. А. Д. Мурадов, М. И. Ким, А. И. Купчишин. Материалы 9-й междунар. конф. “Взаимодействие излучений с твердым телом”, 20-22 сентября 2011 г., Минск, БГУ (2011) 150-153

13. E. Lee, S. Yoon, Y. M. Um, W. Jo, C. W. Seo, H. Cheong, B. J. Kim, H. G. Lee, G. W. Hong. Physica C, 463-465 (2007) 732-735

14. V. A. Maroni, J. L. Reeves. Appl. Spectr., 61, N 4 (2007) 1-8

15. А. И. Купчишин, А. Д. Мурадов, Ж. А. Омарбекова, Б. Г. Таипова. Изв. вузов. Сер. Физика, 50, № 2 (2007) 52-58

16. Ф. Ф. Комаров, А. И. Купчишин, А. Д. Мурадов, М. И. Ким, А. В. Леонтьев. Журн. прикл. спектр., 79, № 6 (2012) 902-906 [F. F. Komarov, A. I. Kupchishin, A. D. Muradov, M. I. Kim, A. V. Leontyev. J. Appl. Spectr., 79, N 6 (2012) 896-900]