A SIMPLE METHOD TO EVALUATE THE PURITY OF SYNTHETIC HYDROXYAPATITE GRANULES
Abstract
Using a method based on the spectrophotometric analysis of the liquids remaining after washing ceramic granules, the type of impurity was determined, the wavelength for measuring the impurity was established, and the type of cell (polystyrene or quartz) was analyzed. The absorbance of the samples was measured at wavelengths between 190 and 1100 nm. The results showed that both cuvette types are useful; however, the greatest absorbances were detected using quartz ones at low wavelengths around 190 nm. The comparison of absorption spectra from the samples, centrifuged and non-centrifuged, enabled us to define the impurities as small apatite particles.
Supporting agencies: The authors would like to acknowledge financial assistance for this research from the Ministry of Science and Higher Education in Poland awarded (MNmb 3) and the DS 2 project of the Medical University of Lublin. The paper was developed using equipment purchased through agreement No. POPW.01.03.00-06-010/09-00 of the Operational Program Development of Eastern Poland.
About the Authors
L. Borkowski
Medical University of Lublin
Poland
Poland
Chair and Department of Biochemistry and Biotechnology
Chodzki 1, 20-093 LublinM. Wojcik
Medical University of Lublin
Poland
Poland
Chair and Department of Biochemistry and Biotechnology
Chodzki 1, 20-093 LublinG. Ginalska
Medical University of Lublin
Poland
Poland
Chair and Department of Biochemistry and Biotechnology
Chodzki 1, 20-093 LublinReferences
1. Z. Shi, X. Huang, Y. Cai, R. Tang, D. Yang, Acta Biomater., 5, 338–345 (2009).
2. M. Motskin, D. M. Wright, K. Muller, N. Kyle, T. G. Gard, A. E. Porter, J. N. Skepper, Biomaterials, 30, 3307–3317 (2009).
3. M. F. Hsieh, L. H. Perng, T. S. Chin, H. G. Perng, Biomaterials, 22, 2601–2607 (2001).
4. A. Jillavenkatesa, R. A. Condrate Sr., J. Mater. Sci., 33, 4111–4119 (1998).
5. S. Sakai, T. Anada, K. Tsuchiya, H. Yamazaki, H.C. Margolis, O. Suzuki, Dent. Mater. J., 35, 216–224 (2016).
6. A. Sroka-Bartnicka, L. Borkowski, G. Ginalska, A. Slosarczyk, S.G. Kazarian, Spectrochim. Acta A, 171, 155–161 (2017).
7. A. Slosarczyk, Z. Paszkiewicz, C. Paluszkiewicz, J. Mol. Struct., 744, 657–661 (2005).
8. L. Borkowski, A. Sroka-Bartnicka, P. Draczkowski, A. Ptak, E. Zieba, A. Slosarczyk, G. Ginalska, Mat. Sci. Eng. C:Mater., 62, 260–267 (2016).
9. M. Kazanci, P. Fratzl, K. Klaushofer, E. P. Paschalis, Calcified Tissue Int., 79, 354–359 (2006).
10. I. Mobasherpour, M.S. Heshajin, A. Kazemzadeh, M. Zakeri, J. Alloy Compd., 430, 330–333 (2007).
11. A. Farzadi, F. Bakhshi, M. Solati-Hashjin, M. Asadi-Eydivand, N. A. Osman, Ceram. Int., 40, 6021–6029 (2014).
12. K. P. Tank, P. Sharma, D. K. Kanchan, M. J. Joshi, Cryst. Res. Technol., 46, 1309–1316 (2011).
13. S. Joschek, B. Nies, R. Krotz, A. Gopferich, Biomaterials, 21, 1645–1658 (2000).
14. A. Stoch, W. Jastrzebski, E. Długon, W. Lejda, B. Trybalska, G. J. Stoch, A. Adamczyk, J. Mol. Struct., 744, 633–640 (2005).
15. K. A. Hing, S. M. Best, W. Bonfield, J. Mater. Sci:Mater., 10, 135–145 (2005).
16. Y. Shen, J. Liu, K. Lin, W. Zhang, Mater. Lett., 70, 76–79 (2012).
17. R. N. Panda, M. F. Hsieh, R. J. Chung, T. S. Chin, J. Phys.Chem. Solids, 64, 193–199 (2003).
18. C. Jäger, T. Welzel, W. Meyer-Zaika, M. Epple, Magn. Reson. Chem., 44, 573–580 (2006).
19. A. K. Nayak, Int. J. Chem. Tech. Res., 2, 903–907 (2010).
20. V. P. Orlovskii, V. S. Komlev, S. M. Barinov, Inorg. Mater., 38, 973–984 (2002).
21. L. Bernard, M. Freche, J. L. Lacout, B. Biscans, Powder Technol., 103, 19–25 (1999).
Review
For citations:
Borkowski L., Wojcik M., Ginalska G. A SIMPLE METHOD TO EVALUATE THE PURITY OF SYNTHETIC HYDROXYAPATITE GRANULES. Zhurnal Prikladnoii Spektroskopii. 2019;86(5):802-806.
Views: 302
Email this article 